National Guard Epoxy Flooring Top Coat S F

Of coats x dft microns national guard primer for cement clear 1 x 40 national guard epoxy flooring topcoat 2 x 70 100 for antiskidding spread aggregates when first coat is wet.

National guard epoxy flooring top coat s f.

National guard flexible epoxy flooring clear s f. Apply second coat as a topcoat after 8 hrs. 1 x 300 national guard flexible epoxy flooring topcoat. Of coats x dft micron national guard primer for cement clear.

After drying apply second coat. Flash point mixed shelf life 30 c above 100 c. 2 x 75 for antiskidding spread recommended size aggregates when first coat is wet. Apply second coat as a top coat after 8 hrs.

National guard epoxy flooring topcoat s f. Of coats x dft microns national guard primer for cement clear 1 x 40 national guard epoxy flooring topcoat 1 2 x 300 for antiskidding spread aggregates when first coat is wet. The fully cured film has good adhesion excellent chemical resistance and good abrasion and impact resistances. National guard epoxy flooring topcoat s f.

Two pack epoxy coating with long pot life very good resistance to corrosion splash and spillage of mild chemicals and solvents. The fully cured film has good adhesion to concrete floors and good resistance to water. 1 2 coats for antiskidding spread aggregates when first coat is wet. 1 coat national guard epoxy flooring topcoat s f.

1 x 40 national guard epoxy flooring topcoat. Apply second coat as a topcoat after 16 hours. Apply second coat as a top coat after 8 hrs. 1 2 x 300 for anti skidding spread uniformly aggregates when first coat is wet.

National guard primer for cement. 150 microns coat fla sh point 100 c drying time drying time 30 c temperature humidity air movement film thickness and number of coats all affect the drying time touch dry 3 4 hours dry to recoat 8 hours minimum 72 hours maximum fully cured 7 days advantages national guard epoxy flooring primer s f. It has very good flow and leveling properties good water resistance good abrasion and impact resistance. For exposed area of applications overcoat above system with polyurethane coatings.

A two pack chemical resistant high build solvent free topcoat based on polyamine cured epoxy resin for concrete floors. It has good flow and resistant to splash and spillage of mild chemicals and solvents.